Highly carbonized iron, the direct product of the blast
furnace; -- used for making castings, and for conversion into wrought
iron and steel. It can not be welded or forged, is brittle, and
sometimes very hard. Besides carbon, it contains sulphur, phosphorus,
silica, etc.